Standard: ASME SB335
Other Standard: GB, AISI, ASTM/ASME, DIN, EN, JIS
Shapes: Plates/ Sheets
Width: 0mm ~ 2500mm
Surface Treatment(Finish): Mirror, Brushed, Mill Finished, Polished, Pickling,Pickling + sandblasting
Standard: ASME SB335
Other Standard: GB, AISI, ASTM/ASME, DIN, EN, JIS
Shapes: Plates/ Sheets
Width: 0mm ~ 2500mm
Surface Treatment(Finish): Mirror, Brushed, Mill Finished, Polished, Pickling,Pickling + sandblasting
| Hastelloy | Density (g/cm3) | Melting point (℃) | Elongation A5 (%) | Tensile Strength (Rm N/mm2) | Yield Strength (RP0.2N/mm2) | Rockwell Hardness |
| C-4 | 8.6 | 1335-1380℃ | 40 | 690 | 276 | 85-95 HRB |
Type: Cold finished(cold rolled), Hot finished( Hot rolled)
Thickness of Plates: 4.76mm ~ 60mm (Hot Rolled), Width: 0mm ~ 2500mm
Thickness of Sheet: 1.00mm ~ 4.76mm (Cold Rolled), Width: 0mm ~ 1500mm
Surface Treatment(Finish): Mirror, Brushed, Mill Finished, Polished, Pickling,Pickling + sandblasting
Edge:Grinding, cutting
Melting method: Vacuum Induction Melting (VIM) + Electroslag Remelting (ESR); or VIM + VAR
Inspection: TUV, SGS,
Packing: Wooden box, Waterproof polybag
Application:
Nickel-based alloy C-4 thick plates are primarily used in key hot-end components operating at temperatures above 650 °C in strongly oxidizing environments, such as heat-treatment furnace structures, high-temperature chemical equipment, and aircraft-engine parts.
C-4 thin sheets are used for applications such as high-temperature oxidation-resistant coatings, linings, seals, and precision-formed parts. They are often used in aerospace, energy, and high-temperature industrial applications that require thermal stability and lightweight design.